Wang, X.; Xiao, C.; Zheng, P.; Zhao, Z.; Alabsi, M.H.; Shi, Y.; Gao, D.; Duan, A.; Huang, K.W.; Xu, C.: Dendritic micro-mesoporous composites with center-radial pores assembled by TS-1 nanocrystals to enhance hydrodesulfurization activity of dibenzothiophene and 4,6-dimethyldibenzothiophene. Journal of Catalysis 384 (2020), p. 136-146
10.1016/j.jcat.2020.02.013
Open Access Version (externer Anbieter)
Abstract:
A novel dendritic composite (TD) with an open center-radial pore structure using TS-1 nanocrystals as microporous precursors was successfully synthesized by a facile method. TS-1 nanocrystals were embedded into the framework of dendritic mesoporous silica nanospheres (DMSNs) to form Si–O–Ti bonds, which was beneficial for generating more S vacancies of MoS2 active phases. The NiMo/TD-2 catalyst had a larger surface area and stronger metal–support interaction, resulting in higher sulfidation and dispersion degrees of MoS2 active phases over the sulfided NiMo/TD-2 catalyst, which was consequently favored to improve the hydrodesulfurization (HDS) activity of dibenzothiophene (DBT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT). Furthermore, the NiMo/TD-2 catalyst with an SiO2/TiO2 molar ratio of 150 exhibited higher HDS performance for DBT and 4,6-DMDBT than other NiMo/TD catalysts and the commercial NiMo/Al2O3 catalyst. Moreover, the NiMo/TD-2 catalyst possessed more Brønsted and Lewis acid sites, thus promoting the hydrogenation of DBT and the isomerization of 4,6-DMDBT.