• Yu, Y.; Mao, Q.; Wong, D.; Gao, R.; Zheng, L.; Yang, W.; Yang, J.; Zhang, N.; Li, Z.; Schulz, C.; Liu, X.: Ribbon-Ordered Superlattice Enables Reversible Anion Redox and Stable High-Voltage Na-Ion Battery Cathodes. Journal of the American Chemical Society 146 (2024), p. 22220–22235

10.1021/jacs.4c02782

Abstract:
High-voltage layered oxide cathodes attract great attention for sodium-ion batteries (SIBs) due to the potential high energy density, but high voltage usually leads to rapid capacity decay. Herein, a stable high-voltage NaLi0.1Ni0.35Mn0.3Ti0.25O2 cathode with a ribbon-ordered superlattice is reported, and the intrinsic coupling mechanism between structure evolution and the anion redox reaction (ARR) is revealed. Li introduction constructs a special Li–O–Na configuration activating reversible nonbonded O 2p (|O2p)-type ARR and regulates the structure evolution way, enabling the reversible Li ions out-of-layer migration instead of the irreversible transition metal ions out-of-layer migration. The reversible structure evolution enhances the reversibility of the bonded O 2p (O2p)-type ARR and inhibits the generation of oxygen dimers, thus suppressing the irreversible molecular oxygen (O2)-type ARR. After the structure regulation, the structure evolution becomes reversible, |O2p-type ARR is activated, O2p-type ARR becomes stable, and O2-type ARR is inhibited, which largely suppresses the capacity degradation and voltage decay. The discharge capacity is increased from 154 to 168 mA h g–1, the capacity retention after 200 cycles significantly increases from 35 to 84%, and the voltage retention increases from 78 to 93%. This study presents some guidance for the design of high-voltage, O3-type oxide cathodes for high-performance SIBs.